Dependency of microstructural parameters and microindentation hardness on the temperature gradient in the In-Bi-Sn ternary alloy with a low melting point

Kaya H., Böyük U., Çadirli E., Ocak Y., Akbulut S., Keşlioǧlu K., ...Daha Fazla

Metals and Materials International, cilt.14, sa.5, ss.575-582, 2008 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 14 Sayı: 5
  • Basım Tarihi: 2008
  • Doi Numarası: 10.3365/met.mat.2008.10.575
  • Dergi Adı: Metals and Materials International
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.575-582
  • Anahtar Kelimeler: directional solidification, eutectic, growth from melt, alloys
  • İstanbul Gelişim Üniversitesi Adresli: Hayır

Özet

The ternary alloy In-21.5 at.% Bi-17.8 at.% Sn, which has a melting point of 60°C, was directionally solidified upward with a constant growth rate (V = 3.2 μm/s) and different temperature gradients (G = 0.91 K/mm to 2.85 K/mm) by using a Bridgman-type directional solidification furnace. The lamellar spacings (λ) and micro-hardness (Hv) were measured from both the transverse and longitudinal sections of the samples. The dependence of the lamellar spacings (λ) and microhardness (Hv) on the temperature gradients (G) were determined by means of linear regression analysis. According to these results, the value of λ decreases as the value of G increases and the value of Hv increases for a constant V. The results obtained in this work are compared with previous similar experimental results obtained for binary or ternary alloys.