Variation of microindentation hardness with solidification and microstructure parameters in the Al based alloys


Kaya H., Çadirli E., Böyük U., Maraşlı N.

Applied Surface Science, vol.255, no.5 PART 2, pp.3071-3078, 2008 (SCI-Expanded) identifier identifier

  • Publication Type: Article / Article
  • Volume: 255 Issue: 5 PART 2
  • Publication Date: 2008
  • Doi Number: 10.1016/j.apsusc.2008.08.080
  • Journal Name: Applied Surface Science
  • Journal Indexes: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Page Numbers: pp.3071-3078
  • Keywords: Al-base alloys, Microstructures, Hall-Petch relationships, Microindentation hardness
  • Istanbul Gelisim University Affiliated: No

Abstract

The Al based alloys (Al-3 wt%Si, Al-3 wt%Cu and Al-1 wt%Ti) were prepared using metals of 99.99% high purity in the vacuum atmosphere. These alloys were directionally solidified upward with a constant growth rate (V = 0.008 mm/s) at the different temperature gradients (G = 1.1-6.8 K/mm) and also with a constant temperature gradient (G) in a wide range of growth rates (0.008-0.499 mm/s) with a Bridgman type directional solidification furnace. The microstructure parameters (primary dendrite arm spacing, λ 1 , secondary dendrite arm spacing, λ 2 , dendrite tip radius, R, and mushy zone depth, d, were measured from both transverse and longitudinal section of the specimens as a function of G and V. The dependence of microhardness (H V ) on the solidification process parameters (V and G) and the microstructure parameters were determined by using linear regression analysis in the Al based alloys. The results obtained in this work have been compared with the previous similar experimental results obtained for binary or ternary alloys. © 2008 Elsevier B.V. All rights reserved.